N07716 Nickel vs. AWS BVAg-32

N07716 nickel belongs to the nickel alloys classification, while AWS BVAg-32 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is N07716 nickel and the bottom bar is AWS BVAg-32.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
93
Poisson's Ratio 0.29
0.37
Shear Modulus, GPa 78
34
Tensile Strength: Ultimate (UTS), MPa 860
180

Thermal Properties

Latent Heat of Fusion, J/g 320
140
Melting Completion (Liquidus), °C 1480
950
Melting Onset (Solidus), °C 1430
900
Specific Heat Capacity, J/kg-K 440
270
Thermal Expansion, µm/m-K 13
17

Otherwise Unclassified Properties

Density, g/cm3 8.5
11

Common Calculations

Stiffness to Weight: Axial, points 13
4.9
Stiffness to Weight: Bending, points 23
14
Strength to Weight: Axial, points 28
4.7
Strength to Weight: Bending, points 24
6.7
Thermal Shock Resistance, points 24
8.0

Alloy Composition

Aluminum (Al), % 0 to 0.35
0
Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0 to 0.030
0 to 0.0050
Chromium (Cr), % 19 to 22
0
Copper (Cu), % 0
20 to 22
Iron (Fe), % 0 to 11.3
0
Lead (Pb), % 0
0 to 0.0020
Manganese (Mn), % 0 to 0.2
0
Molybdenum (Mo), % 7.0 to 9.5
0
Nickel (Ni), % 59 to 63
0
Niobium (Nb), % 2.8 to 4.0
0
Palladium (Pd), % 0
23 to 27
Phosphorus (P), % 0 to 0.015
0 to 0.0020
Silicon (Si), % 0 to 0.2
0
Silver (Ag), % 0
53 to 55
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 1.0 to 1.6
0
Zinc (Zn), % 0
0 to 0.0010