N07716 Nickel vs. AWS ER80S-Ni1

N07716 nickel belongs to the nickel alloys classification, while AWS ER80S-Ni1 belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N07716 nickel and the bottom bar is AWS ER80S-Ni1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
27
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 78
72
Tensile Strength: Ultimate (UTS), MPa 860
630
Tensile Strength: Yield (Proof), MPa 350
530

Thermal Properties

Latent Heat of Fusion, J/g 320
260
Melting Completion (Liquidus), °C 1480
1450
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 11
41
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 75
2.7
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 13
1.6
Embodied Energy, MJ/kg 190
21
Embodied Water, L/kg 280
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
160
Resilience: Unit (Modulus of Resilience), kJ/m3 300
740
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 28
22
Strength to Weight: Bending, points 24
21
Thermal Diffusivity, mm2/s 2.8
11
Thermal Shock Resistance, points 24
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.35
0
Carbon (C), % 0 to 0.030
0 to 0.12
Chromium (Cr), % 19 to 22
0 to 0.15
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 0 to 11.3
95.3 to 98.8
Manganese (Mn), % 0 to 0.2
0 to 1.3
Molybdenum (Mo), % 7.0 to 9.5
0 to 0.35
Nickel (Ni), % 59 to 63
0.8 to 1.1
Niobium (Nb), % 2.8 to 4.0
0
Phosphorus (P), % 0 to 0.015
0 to 0.025
Silicon (Si), % 0 to 0.2
0.4 to 0.8
Sulfur (S), % 0 to 0.010
0 to 0.025
Titanium (Ti), % 1.0 to 1.6
0
Vanadium (V), % 0
0 to 0.050
Residuals, % 0
0 to 0.5