N07716 Nickel vs. EN 1.4539 Stainless Steel

N07716 nickel belongs to the nickel alloys classification, while EN 1.4539 stainless steel belongs to the iron alloys. They have 55% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N07716 nickel and the bottom bar is EN 1.4539 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
38
Fatigue Strength, MPa 690
220
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 78
79
Shear Strength, MPa 580
430
Tensile Strength: Ultimate (UTS), MPa 860
630
Tensile Strength: Yield (Proof), MPa 350
260

Thermal Properties

Latent Heat of Fusion, J/g 320
300
Maximum Temperature: Mechanical, °C 980
1100
Melting Completion (Liquidus), °C 1480
1440
Melting Onset (Solidus), °C 1430
1390
Specific Heat Capacity, J/kg-K 440
460
Thermal Conductivity, W/m-K 11
12
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 75
31
Density, g/cm3 8.5
8.1
Embodied Carbon, kg CO2/kg material 13
5.7
Embodied Energy, MJ/kg 190
78
Embodied Water, L/kg 280
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
190
Resilience: Unit (Modulus of Resilience), kJ/m3 300
160
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 28
22
Strength to Weight: Bending, points 24
20
Thermal Diffusivity, mm2/s 2.8
3.2
Thermal Shock Resistance, points 24
14

Alloy Composition

Aluminum (Al), % 0 to 0.35
0
Carbon (C), % 0 to 0.030
0 to 0.020
Chromium (Cr), % 19 to 22
19 to 21
Copper (Cu), % 0
1.2 to 2.0
Iron (Fe), % 0 to 11.3
43.1 to 51.8
Manganese (Mn), % 0 to 0.2
0 to 2.0
Molybdenum (Mo), % 7.0 to 9.5
4.0 to 5.0
Nickel (Ni), % 59 to 63
24 to 26
Niobium (Nb), % 2.8 to 4.0
0
Nitrogen (N), % 0
0 to 0.15
Phosphorus (P), % 0 to 0.015
0 to 0.030
Silicon (Si), % 0 to 0.2
0 to 0.7
Sulfur (S), % 0 to 0.010
0 to 0.010
Titanium (Ti), % 1.0 to 1.6
0