N07716 Nickel vs. EN 1.5636 Steel

N07716 nickel belongs to the nickel alloys classification, while EN 1.5636 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is N07716 nickel and the bottom bar is EN 1.5636 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
27
Fatigue Strength, MPa 690
230
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 860
560
Tensile Strength: Yield (Proof), MPa 350
310

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 980
410
Melting Completion (Liquidus), °C 1480
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 11
52
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 75
3.6
Density, g/cm3 8.5
7.9
Embodied Carbon, kg CO2/kg material 13
1.7
Embodied Energy, MJ/kg 190
23
Embodied Water, L/kg 280
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
130
Resilience: Unit (Modulus of Resilience), kJ/m3 300
260
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 28
20
Strength to Weight: Bending, points 24
19
Thermal Diffusivity, mm2/s 2.8
14
Thermal Shock Resistance, points 24
16

Alloy Composition

Aluminum (Al), % 0 to 0.35
0
Carbon (C), % 0 to 0.030
0.060 to 0.12
Chromium (Cr), % 19 to 22
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 0 to 11.3
94.6 to 97.4
Manganese (Mn), % 0 to 0.2
0.5 to 0.8
Molybdenum (Mo), % 7.0 to 9.5
0 to 0.2
Nickel (Ni), % 59 to 63
2.0 to 3.0
Niobium (Nb), % 2.8 to 4.0
0
Phosphorus (P), % 0 to 0.015
0 to 0.020
Silicon (Si), % 0 to 0.2
0 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 1.0 to 1.6
0
Vanadium (V), % 0
0 to 0.050