Both N07716 nickel and EN 2.4669 nickel are nickel alloys. They have 85% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is N07716 nickel and the bottom bar is EN 2.4669 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
16
Fatigue Strength, MPa 690
390
Poisson's Ratio 0.29
0.29
Reduction in Area, % 46
31
Shear Modulus, GPa 78
73
Shear Strength, MPa 580
680
Tensile Strength: Ultimate (UTS), MPa 860
1110
Tensile Strength: Yield (Proof), MPa 350
720

Thermal Properties

Latent Heat of Fusion, J/g 320
310
Maximum Temperature: Mechanical, °C 980
960
Melting Completion (Liquidus), °C 1480
1380
Melting Onset (Solidus), °C 1430
1330
Specific Heat Capacity, J/kg-K 440
460
Thermal Conductivity, W/m-K 11
12
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 75
60
Density, g/cm3 8.5
8.4
Embodied Carbon, kg CO2/kg material 13
10
Embodied Energy, MJ/kg 190
150
Embodied Water, L/kg 280
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
160
Resilience: Unit (Modulus of Resilience), kJ/m3 300
1380
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 28
37
Strength to Weight: Bending, points 24
28
Thermal Diffusivity, mm2/s 2.8
3.1
Thermal Shock Resistance, points 24
33

Alloy Composition

Aluminum (Al), % 0 to 0.35
0.4 to 1.0
Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 19 to 22
14 to 17
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 0 to 11.3
5.0 to 9.0
Manganese (Mn), % 0 to 0.2
0 to 1.0
Molybdenum (Mo), % 7.0 to 9.5
0
Nickel (Ni), % 59 to 63
65.9 to 77.7
Niobium (Nb), % 2.8 to 4.0
0.7 to 1.2
Phosphorus (P), % 0 to 0.015
0 to 0.020
Silicon (Si), % 0 to 0.2
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 1.0 to 1.6
2.3 to 2.8