N07716 Nickel vs. Grade 3 Babbitt Metal

N07716 nickel belongs to the nickel alloys classification, while grade 3 Babbitt Metal belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is N07716 nickel and the bottom bar is grade 3 Babbitt Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
56
Poisson's Ratio 0.29
0.35
Shear Modulus, GPa 78
21
Tensile Strength: Yield (Proof), MPa 350
46

Thermal Properties

Latent Heat of Fusion, J/g 320
79
Melting Completion (Liquidus), °C 1480
420
Melting Onset (Solidus), °C 1430
240
Specific Heat Capacity, J/kg-K 440
230
Thermal Expansion, µm/m-K 13
21

Otherwise Unclassified Properties

Base Metal Price, % relative 75
70
Density, g/cm3 8.5
7.4
Embodied Carbon, kg CO2/kg material 13
12
Embodied Energy, MJ/kg 190
200
Embodied Water, L/kg 280
1210

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 300
19
Stiffness to Weight: Axial, points 13
4.2
Stiffness to Weight: Bending, points 23
17

Alloy Composition

Aluminum (Al), % 0 to 0.35
0 to 0.0050
Antimony (Sb), % 0
7.5 to 8.5
Arsenic (As), % 0
0 to 0.1
Bismuth (Bi), % 0
0 to 0.080
Cadmium (Cd), % 0
0 to 0.050
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 19 to 22
0
Copper (Cu), % 0
7.5 to 8.5
Iron (Fe), % 0 to 11.3
0 to 0.080
Lead (Pb), % 0
0 to 0.35
Manganese (Mn), % 0 to 0.2
0
Molybdenum (Mo), % 7.0 to 9.5
0
Nickel (Ni), % 59 to 63
0
Niobium (Nb), % 2.8 to 4.0
0
Phosphorus (P), % 0 to 0.015
0
Silicon (Si), % 0 to 0.2
0
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
82.3 to 85
Titanium (Ti), % 1.0 to 1.6
0
Zinc (Zn), % 0
0 to 0.0050