N07716 Nickel vs. Grade 360 Molybdenum

N07716 nickel belongs to the nickel alloys classification, while grade 360 molybdenum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is N07716 nickel and the bottom bar is grade 360 molybdenum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
310
Elongation at Break, % 34
6.3 to 17
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 78
120
Tensile Strength: Ultimate (UTS), MPa 860
430 to 620
Tensile Strength: Yield (Proof), MPa 350
270 to 530

Thermal Properties

Latent Heat of Fusion, J/g 320
370
Specific Heat Capacity, J/kg-K 440
250
Thermal Expansion, µm/m-K 13
7.0

Otherwise Unclassified Properties

Density, g/cm3 8.5
10
Embodied Carbon, kg CO2/kg material 13
28
Embodied Energy, MJ/kg 190
330
Embodied Water, L/kg 280
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
37 to 64
Resilience: Unit (Modulus of Resilience), kJ/m3 300
120 to 450
Stiffness to Weight: Axial, points 13
17
Stiffness to Weight: Bending, points 23
22
Strength to Weight: Axial, points 28
12 to 17
Strength to Weight: Bending, points 24
12 to 16
Thermal Shock Resistance, points 24
14 to 21

Alloy Composition

Aluminum (Al), % 0 to 0.35
0
Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 19 to 22
0
Iron (Fe), % 0 to 11.3
0 to 0.010
Manganese (Mn), % 0 to 0.2
0
Molybdenum (Mo), % 7.0 to 9.5
99.9 to 100
Nickel (Ni), % 59 to 63
0 to 0.0020
Niobium (Nb), % 2.8 to 4.0
0
Nitrogen (N), % 0
0 to 0.0020
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.015
0
Silicon (Si), % 0 to 0.2
0 to 0.010
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 1.0 to 1.6
0