N07716 Nickel vs. SAE-AISI 1151 Steel

N07716 nickel belongs to the nickel alloys classification, while SAE-AISI 1151 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is N07716 nickel and the bottom bar is SAE-AISI 1151 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
11 to 17
Fatigue Strength, MPa 690
260 to 410
Poisson's Ratio 0.29
0.29
Reduction in Area, % 46
34 to 40
Shear Modulus, GPa 78
72
Shear Strength, MPa 580
430 to 480
Tensile Strength: Ultimate (UTS), MPa 860
710 to 800
Tensile Strength: Yield (Proof), MPa 350
390 to 660

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 980
400
Melting Completion (Liquidus), °C 1480
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 11
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
10
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
12

Otherwise Unclassified Properties

Base Metal Price, % relative 75
1.8
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 13
1.4
Embodied Energy, MJ/kg 190
18
Embodied Water, L/kg 280
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
86 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 300
400 to 1170
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 28
25 to 28
Strength to Weight: Bending, points 24
22 to 24
Thermal Diffusivity, mm2/s 2.8
14
Thermal Shock Resistance, points 24
22 to 25

Alloy Composition

Aluminum (Al), % 0 to 0.35
0
Carbon (C), % 0 to 0.030
0.48 to 0.55
Chromium (Cr), % 19 to 22
0
Iron (Fe), % 0 to 11.3
98.3 to 98.7
Manganese (Mn), % 0 to 0.2
0.7 to 1.0
Molybdenum (Mo), % 7.0 to 9.5
0
Nickel (Ni), % 59 to 63
0
Niobium (Nb), % 2.8 to 4.0
0
Phosphorus (P), % 0 to 0.015
0 to 0.040
Silicon (Si), % 0 to 0.2
0
Sulfur (S), % 0 to 0.010
0.080 to 0.13
Titanium (Ti), % 1.0 to 1.6
0