N07716 Nickel vs. N08800 Stainless Steel

N07716 nickel belongs to the nickel alloys classification, while N08800 stainless steel belongs to the iron alloys. They have 59% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N07716 nickel and the bottom bar is N08800 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
4.5 to 34
Fatigue Strength, MPa 690
150 to 390
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 78
77
Shear Strength, MPa 580
340 to 580
Tensile Strength: Ultimate (UTS), MPa 860
500 to 1000
Tensile Strength: Yield (Proof), MPa 350
190 to 830

Thermal Properties

Latent Heat of Fusion, J/g 320
300
Maximum Temperature: Mechanical, °C 980
1100
Melting Completion (Liquidus), °C 1480
1390
Melting Onset (Solidus), °C 1430
1360
Specific Heat Capacity, J/kg-K 440
480
Thermal Conductivity, W/m-K 11
12
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 75
30
Density, g/cm3 8.5
8.0
Embodied Carbon, kg CO2/kg material 13
5.3
Embodied Energy, MJ/kg 190
76
Embodied Water, L/kg 280
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
42 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 300
96 to 1740
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 28
18 to 35
Strength to Weight: Bending, points 24
18 to 28
Thermal Diffusivity, mm2/s 2.8
3.0
Thermal Shock Resistance, points 24
13 to 25

Alloy Composition

Aluminum (Al), % 0 to 0.35
0.15 to 0.6
Carbon (C), % 0 to 0.030
0 to 0.1
Chromium (Cr), % 19 to 22
19 to 23
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 0 to 11.3
39.5 to 50.7
Manganese (Mn), % 0 to 0.2
0 to 1.5
Molybdenum (Mo), % 7.0 to 9.5
0
Nickel (Ni), % 59 to 63
30 to 35
Niobium (Nb), % 2.8 to 4.0
0
Phosphorus (P), % 0 to 0.015
0 to 0.045
Silicon (Si), % 0 to 0.2
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 1.0 to 1.6
0.15 to 0.6