N07716 Nickel vs. Z41321 Zinc

N07716 nickel belongs to the nickel alloys classification, while Z41321 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is N07716 nickel and the bottom bar is Z41321 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
87
Elongation at Break, % 34
60
Poisson's Ratio 0.29
0.25
Shear Modulus, GPa 78
35
Tensile Strength: Ultimate (UTS), MPa 860
190
Tensile Strength: Yield (Proof), MPa 350
150

Thermal Properties

Latent Heat of Fusion, J/g 320
110
Maximum Temperature: Mechanical, °C 980
90
Melting Completion (Liquidus), °C 1480
410
Melting Onset (Solidus), °C 1430
400
Specific Heat Capacity, J/kg-K 440
390
Thermal Conductivity, W/m-K 11
110
Thermal Expansion, µm/m-K 13
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
27
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
37

Otherwise Unclassified Properties

Base Metal Price, % relative 75
12
Density, g/cm3 8.5
6.6
Embodied Carbon, kg CO2/kg material 13
2.8
Embodied Energy, MJ/kg 190
54
Embodied Water, L/kg 280
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
100
Resilience: Unit (Modulus of Resilience), kJ/m3 300
130
Stiffness to Weight: Axial, points 13
7.4
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 28
7.9
Strength to Weight: Bending, points 24
11
Thermal Diffusivity, mm2/s 2.8
44
Thermal Shock Resistance, points 24
5.9

Alloy Composition

Aluminum (Al), % 0 to 0.35
0 to 0.010
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 19 to 22
0
Copper (Cu), % 0
0.5 to 1.0
Iron (Fe), % 0 to 11.3
0 to 0.010
Lead (Pb), % 0
0 to 0.010
Manganese (Mn), % 0 to 0.2
0
Molybdenum (Mo), % 7.0 to 9.5
0
Nickel (Ni), % 59 to 63
0
Niobium (Nb), % 2.8 to 4.0
0
Phosphorus (P), % 0 to 0.015
0
Silicon (Si), % 0 to 0.2
0
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 1.0 to 1.6
0.080 to 0.18
Zinc (Zn), % 0
98.8 to 99.42