N07752 Nickel vs. AWS BVAg-6b
N07752 nickel belongs to the nickel alloys classification, while AWS BVAg-6b belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is N07752 nickel and the bottom bar is AWS BVAg-6b.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 93 |
| Poisson's Ratio | 0.29 | |
| 0.35 |
| Shear Modulus, GPa | 73 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 1120 | |
| 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 160 |
| Melting Completion (Liquidus), °C | 1380 | |
| 870 |
| Melting Onset (Solidus), °C | 1330 | |
| 780 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 310 |
| Thermal Expansion, µm/m-K | 12 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 9.7 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 49 |
| Embodied Energy, MJ/kg | 150 | |
| 770 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 5.3 |
| Stiffness to Weight: Bending, points | 23 | |
| 16 |
| Strength to Weight: Axial, points | 37 | |
| 5.1 |
| Strength to Weight: Bending, points | 29 | |
| 7.3 |
| Thermal Shock Resistance, points | 34 | |
| 7.4 |
Alloy Composition
| Aluminum (Al), % | 0.4 to 1.0 | |
| 0 |
| Boron (B), % | 0 to 0.0070 | |
| 0 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0010 |
| Carbon (C), % | 0.020 to 0.060 | |
| 0 to 0.0050 |
| Chromium (Cr), % | 14.5 to 17 | |
| 0 |
| Cobalt (Co), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 49 to 51 |
| Iron (Fe), % | 5.0 to 9.0 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.0020 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 70 to 77.1 | |
| 0 |
| Niobium (Nb), % | 0.7 to 1.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.0080 | |
| 0 to 0.0020 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Silver (Ag), % | 0 | |
| 49 to 51 |
| Sulfur (S), % | 0 to 0.0030 | |
| 0 |
| Titanium (Ti), % | 2.3 to 2.8 | |
| 0 |
| Vanadium (V), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.050 | |
| 0 to 0.0010 |