N07752 Nickel vs. Grade CW6M Nickel

Both N07752 nickel and grade CW6M nickel are nickel alloys. They have 78% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N07752 nickel and the bottom bar is grade CW6M nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 22
29
Fatigue Strength, MPa 450
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
84
Tensile Strength: Ultimate (UTS), MPa 1120
560
Tensile Strength: Yield (Proof), MPa 740
310

Thermal Properties

Latent Heat of Fusion, J/g 310
330
Maximum Temperature: Mechanical, °C 960
970
Melting Completion (Liquidus), °C 1380
1530
Melting Onset (Solidus), °C 1330
1470
Specific Heat Capacity, J/kg-K 460
430
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 60
65
Density, g/cm3 8.4
8.8
Embodied Carbon, kg CO2/kg material 10
13
Embodied Energy, MJ/kg 150
170
Embodied Water, L/kg 260
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
140
Resilience: Unit (Modulus of Resilience), kJ/m3 1450
220
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 37
18
Strength to Weight: Bending, points 29
17
Thermal Shock Resistance, points 34
16

Alloy Composition

Aluminum (Al), % 0.4 to 1.0
0
Boron (B), % 0 to 0.0070
0
Carbon (C), % 0.020 to 0.060
0 to 0.070
Chromium (Cr), % 14.5 to 17
17 to 20
Cobalt (Co), % 0 to 0.050
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 5.0 to 9.0
0 to 3.0
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 0
17 to 20
Nickel (Ni), % 70 to 77.1
54.9 to 66
Niobium (Nb), % 0.7 to 1.2
0
Phosphorus (P), % 0 to 0.0080
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.0030
0 to 0.030
Titanium (Ti), % 2.3 to 2.8
0
Vanadium (V), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.050
0