N10629 Nickel vs. AWS BAg-13

N10629 nickel belongs to the nickel alloys classification, while AWS BAg-13 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is N10629 nickel and the bottom bar is AWS BAg-13.

UNS N10629 Nickel-Molybdenum Alloy AWS BAg-13 (P07540) Filler Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		91

Poisson's Ratio		0.31
Poisson's Ratio		0.35

Shear Modulus, GPa		83
Shear Modulus, GPa		34

Tensile Strength: Ultimate (UTS), MPa		860
Tensile Strength: Ultimate (UTS), MPa		180

Thermal Properties

Latent Heat of Fusion, J/g		310
Latent Heat of Fusion, J/g		150

Melting Completion (Liquidus), °C		1610
Melting Completion (Liquidus), °C		860

Melting Onset (Solidus), °C		1560
Melting Onset (Solidus), °C		720

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		310

Thermal Expansion, µm/m-K		10
Thermal Expansion, µm/m-K		19

Otherwise Unclassified Properties

Density, g/cm³		9.2
Density, g/cm³		9.7

Embodied Carbon, kg CO₂/kg material		15
Embodied Carbon, kg CO₂/kg material		52

Embodied Energy, MJ/kg		190
Embodied Energy, MJ/kg		820

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		5.2

Stiffness to Weight: Bending, points		22
Stiffness to Weight: Bending, points		16

Strength to Weight: Axial, points		26
Strength to Weight: Axial, points		5.2

Strength to Weight: Bending, points		22
Strength to Weight: Bending, points		7.3

Thermal Shock Resistance, points		27
Thermal Shock Resistance, points		7.5

Alloy Composition

Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460

Aluminum (Al), %		0.1 to 0.5
Aluminum (Al), %		0

Carbon (C), %		0 to 0.010
Carbon (C), %		0

Chromium (Cr), %		0.5 to 1.5
Chromium (Cr), %		0

Cobalt (Co), %		0 to 2.5
Cobalt (Co), %		0

Copper (Cu), %		0 to 0.5
Copper (Cu), %		37.4 to 42.5

Iron (Fe), %		1.0 to 6.0
Iron (Fe), %		0

Manganese (Mn), %		0 to 1.5
Manganese (Mn), %		0

Molybdenum (Mo), %		26 to 30
Molybdenum (Mo), %		0

Nickel (Ni), %		65 to 72.4
Nickel (Ni), %		0.5 to 1.5

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0

Silicon (Si), %		0 to 0.050
Silicon (Si), %		0

Silver (Ag), %		0
Silver (Ag), %		53 to 55

Sulfur (S), %		0 to 0.010
Sulfur (S), %		0

Zinc (Zn), %		0
Zinc (Zn), %		4.0 to 6.0

Residuals, %		0
Residuals, %		0 to 0.15