R04295 Alloy vs. C75700 Nickel Silver
R04295 alloy belongs to the otherwise unclassified metals classification, while C75700 nickel silver belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is R04295 alloy and the bottom bar is C75700 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Elongation at Break, % | 22 | |
| 3.2 to 22 |
| Poisson's Ratio | 0.38 | |
| 0.32 |
| Shear Modulus, GPa | 37 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 410 | |
| 590 to 610 |
| Tensile Strength: Yield (Proof), MPa | 300 | |
| 470 to 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 200 |
| Specific Heat Capacity, J/kg-K | 260 | |
| 390 |
| Thermal Expansion, µm/m-K | 7.2 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.0 | |
| 8.4 |
| Embodied Water, L/kg | 950 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 84 | |
| 19 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 430 | |
| 930 to 1410 |
| Stiffness to Weight: Axial, points | 6.3 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 17 | |
| 19 |
| Strength to Weight: Axial, points | 13 | |
| 19 to 20 |
| Strength to Weight: Bending, points | 14 | |
| 19 |
| Thermal Shock Resistance, points | 40 | |
| 22 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.015 | |
| 0 |
| Copper (Cu), % | 0 | |
| 63.5 to 66.5 |
| Hafnium (Hf), % | 9.0 to 11 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 11 to 13 |
| Niobium (Nb), % | 85.9 to 90.3 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.025 | |
| 0 |
| Tantalum (Ta), % | 0 to 0.5 | |
| 0 |
| Titanium (Ti), % | 0.7 to 1.3 | |
| 0 |
| Tungsten (W), % | 0 to 0.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 19.2 to 25.5 |
| Zirconium (Zr), % | 0 to 0.7 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |