R05200 Tantalum vs. 6262A Aluminum

R05200 tantalum belongs to the otherwise unclassified metals classification, while 6262A aluminum belongs to the aluminum alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is R05200 tantalum and the bottom bar is 6262A aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
68
Elongation at Break, % 1.1 to 28
4.5 to 11
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 69
26
Tensile Strength: Ultimate (UTS), MPa 210 to 540
310 to 410
Tensile Strength: Yield (Proof), MPa 140 to 390
270 to 370

Thermal Properties

Latent Heat of Fusion, J/g 140
400
Specific Heat Capacity, J/kg-K 140
890
Thermal Conductivity, W/m-K 59
170
Thermal Expansion, µm/m-K 6.5
23

Otherwise Unclassified Properties

Density, g/cm3 17
2.8
Embodied Water, L/kg 650
1190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.5 to 53
17 to 34
Resilience: Unit (Modulus of Resilience), kJ/m3 50 to 420
540 to 1000
Stiffness to Weight: Axial, points 6.2
14
Stiffness to Weight: Bending, points 11
49
Strength to Weight: Axial, points 3.6 to 9.0
31 to 41
Strength to Weight: Bending, points 4.8 to 8.8
36 to 44
Thermal Diffusivity, mm2/s 25
67
Thermal Shock Resistance, points 13 to 32
14 to 18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
94.2 to 97.8
Bismuth (Bi), % 0
0.4 to 0.9
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 0
0.040 to 0.14
Copper (Cu), % 0
0.15 to 0.4
Hydrogen (H), % 0 to 0.0015
0
Iron (Fe), % 0 to 0.010
0 to 0.7
Magnesium (Mg), % 0
0.8 to 1.2
Manganese (Mn), % 0
0 to 0.15
Molybdenum (Mo), % 0 to 0.020
0
Nickel (Ni), % 0 to 0.010
0
Niobium (Nb), % 0 to 0.1
0
Nitrogen (N), % 0 to 0.010
0
Oxygen (O), % 0 to 0.015
0
Silicon (Si), % 0 to 0.0050
0.4 to 0.8
Tantalum (Ta), % 99.8 to 100
0
Tin (Sn), % 0
0.4 to 1.0
Titanium (Ti), % 0 to 0.010
0 to 0.1
Tungsten (W), % 0 to 0.050
0
Zinc (Zn), % 0
0 to 0.25
Residuals, % 0
0 to 0.15