R05255 Alloy vs. 60Pd-40Ag Alloy
Both R05255 alloy and 60Pd-40Ag alloy are otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is R05255 alloy and the bottom bar is 60Pd-40Ag alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 100 |
| Elongation at Break, % | 20 | |
| 1.1 to 28 |
| Poisson's Ratio | 0.34 | |
| 0.38 |
| Shear Modulus, GPa | 70 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 340 to 720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 140 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 240 |
| Thermal Conductivity, W/m-K | 59 | |
| 29 |
| Thermal Expansion, µm/m-K | 6.6 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 11 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.3 | |
| 4.9 |
| Stiffness to Weight: Bending, points | 11 | |
| 14 |
| Strength to Weight: Axial, points | 9.1 | |
| 8.4 to 18 |
| Strength to Weight: Bending, points | 8.9 | |
| 9.6 to 16 |
| Thermal Diffusivity, mm2/s | 25 | |
| 11 |
| Thermal Shock Resistance, points | 31 | |
| 16 to 34 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.1 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Niobium (Nb), % | 0 to 0.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.015 | |
| 0 |
| Palladium (Pd), % | 0 | |
| 59.5 to 60.9 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 |
| Silver (Ag), % | 0 | |
| 39.1 to 40.5 |
| Tantalum (Ta), % | 95.9 to 98 | |
| 0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 |
| Tungsten (W), % | 2.0 to 3.5 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.3 |