R05255 Alloy vs. 90-platinum 10-iridium
Both R05255 alloy and 90-platinum 10-iridium are otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is R05255 alloy and the bottom bar is 90-platinum 10-iridium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 20 | |
| 5.5 to 34 |
| Poisson's Ratio | 0.34 | |
| 0.38 |
| Shear Modulus, GPa | 70 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 330 to 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 100 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 130 |
| Thermal Expansion, µm/m-K | 6.6 | |
| 8.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 22 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.3 | |
| 5.3 |
| Stiffness to Weight: Bending, points | 11 | |
| 9.1 |
| Strength to Weight: Axial, points | 9.1 | |
| 4.2 to 7.1 |
| Strength to Weight: Bending, points | 8.9 | |
| 4.9 to 6.9 |
| Thermal Shock Resistance, points | 31 | |
| 13 to 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iridium (Ir), % | 0 | |
| 9.5 to 10.5 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Niobium (Nb), % | 0 to 0.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.015 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 89.3 to 90.5 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 |
| Tantalum (Ta), % | 95.9 to 98 | |
| 0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 |
| Tungsten (W), % | 2.0 to 3.5 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |