R05255 Alloy vs. C94700 Bronze
R05255 alloy belongs to the otherwise unclassified metals classification, while C94700 bronze belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is R05255 alloy and the bottom bar is C94700 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 20 | |
| 7.9 to 32 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 70 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 350 to 590 |
| Tensile Strength: Yield (Proof), MPa | 450 | |
| 160 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 200 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 380 |
| Thermal Conductivity, W/m-K | 59 | |
| 54 |
| Thermal Expansion, µm/m-K | 6.6 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 8.8 |
| Embodied Water, L/kg | 630 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 | |
| 41 to 89 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 530 | |
| 110 to 700 |
| Stiffness to Weight: Axial, points | 6.3 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 11 | |
| 18 |
| Strength to Weight: Axial, points | 9.1 | |
| 11 to 19 |
| Strength to Weight: Bending, points | 8.9 | |
| 13 to 18 |
| Thermal Diffusivity, mm2/s | 25 | |
| 16 |
| Thermal Shock Resistance, points | 31 | |
| 12 to 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.15 |
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Copper (Cu), % | 0 | |
| 85 to 90 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 | |
| 0 to 0.2 |
| Molybdenum (Mo), % | 0 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 4.5 to 6.0 |
| Niobium (Nb), % | 0 to 0.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.015 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Tantalum (Ta), % | 95.9 to 98 | |
| 0 |
| Tin (Sn), % | 0 | |
| 4.5 to 6.0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 |
| Tungsten (W), % | 2.0 to 3.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 1.0 to 2.5 |
| Residuals, % | 0 | |
| 0 to 1.3 |