R05400 Tantalum vs. EN 1.4415 Stainless Steel

R05400 tantalum belongs to the otherwise unclassified metals classification, while EN 1.4415 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is R05400 tantalum and the bottom bar is EN 1.4415 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 1.1 to 28
17 to 20
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 69
77
Tensile Strength: Ultimate (UTS), MPa 210 to 540
830 to 930
Tensile Strength: Yield (Proof), MPa 140 to 390
730 to 840

Thermal Properties

Latent Heat of Fusion, J/g 140
280
Specific Heat Capacity, J/kg-K 140
470
Thermal Conductivity, W/m-K 59
19
Thermal Expansion, µm/m-K 6.5
9.9

Otherwise Unclassified Properties

Density, g/cm3 17
7.9
Embodied Water, L/kg 650
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.5 to 53
150 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 50 to 420
1350 to 1790
Stiffness to Weight: Axial, points 6.2
14
Stiffness to Weight: Bending, points 11
25
Strength to Weight: Axial, points 3.6 to 9.0
29 to 33
Strength to Weight: Bending, points 4.8 to 8.8
25 to 27
Thermal Diffusivity, mm2/s 25
5.1
Thermal Shock Resistance, points 13 to 32
30 to 34

Alloy Composition

Carbon (C), % 0 to 0.010
0 to 0.030
Chromium (Cr), % 0
11.5 to 13.5
Hydrogen (H), % 0 to 0.0015
0
Iron (Fe), % 0 to 0.010
75.9 to 82.4
Manganese (Mn), % 0
0 to 0.5
Molybdenum (Mo), % 0 to 0.020
1.5 to 2.5
Nickel (Ni), % 0 to 0.010
4.5 to 6.5
Niobium (Nb), % 0 to 0.1
0
Nitrogen (N), % 0 to 0.010
0
Oxygen (O), % 0 to 0.030
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.0050
0 to 0.5
Sulfur (S), % 0
0 to 0.015
Tantalum (Ta), % 99.7 to 100
0
Titanium (Ti), % 0 to 0.010
0 to 0.010
Tungsten (W), % 0 to 0.050
0
Vanadium (V), % 0
0.1 to 0.5

Comparable Variants