R30001 Cobalt vs. ZA-27
R30001 cobalt belongs to the cobalt alloys classification, while ZA-27 belongs to the zinc alloys. There are 24 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is R30001 cobalt and the bottom bar is ZA-27.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 1930 | |
| 260 to 370 |
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 78 |
| Elongation at Break, % | 1.0 | |
| 2.0 to 4.5 |
| Poisson's Ratio | 0.28 | |
| 0.27 |
| Shear Modulus, GPa | 86 | |
| 31 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 400 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 130 |
| Melting Completion (Liquidus), °C | 1530 | |
| 480 |
| Melting Onset (Solidus), °C | 1260 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 530 |
| Thermal Conductivity, W/m-K | 15 | |
| 130 |
| Thermal Expansion, µm/m-K | 11 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.8 | |
| 30 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.8 | |
| 53 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.0 | |
| 5.0 |
| Embodied Carbon, kg CO2/kg material | 8.9 | |
| 4.2 |
| Embodied Energy, MJ/kg | 130 | |
| 80 |
| Embodied Water, L/kg | 460 | |
| 570 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 22 | |
| 28 |
| Strength to Weight: Axial, points | 19 | |
| 22 to 24 |
| Strength to Weight: Bending, points | 18 | |
| 24 to 25 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 47 |
| Thermal Shock Resistance, points | 19 | |
| 14 to 15 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 25 to 28 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Carbon (C), % | 2.0 to 3.0 | |
| 0 |
| Chromium (Cr), % | 28 to 32 | |
| 0 |
| Cobalt (Co), % | 43 to 59 | |
| 0 |
| Copper (Cu), % | 0 | |
| 2.0 to 2.5 |
| Iron (Fe), % | 0 to 3.0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.010 to 0.020 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 0 to 3.0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 2.0 | |
| 0 to 0.080 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Tungsten (W), % | 11 to 13 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 69.3 to 73 |