R30003 Cobalt vs. AWS E219
R30003 cobalt belongs to the cobalt alloys classification, while AWS E219 belongs to the iron alloys. They have 44% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is R30003 cobalt and the bottom bar is AWS E219.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 200 |
| Elongation at Break, % | 10 to 73 | |
| 17 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 83 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 970 to 1720 | |
| 690 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 290 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1400 |
| Melting Onset (Solidus), °C | 1440 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 480 |
| Thermal Conductivity, W/m-K | 13 | |
| 14 |
| Thermal Expansion, µm/m-K | 13 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 95 | |
| 15 |
| Density, g/cm3 | 8.4 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 3.1 |
| Embodied Energy, MJ/kg | 110 | |
| 44 |
| Embodied Water, L/kg | 400 | |
| 160 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 32 to 57 | |
| 25 |
| Strength to Weight: Bending, points | 26 to 38 | |
| 23 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 3.8 |
| Thermal Shock Resistance, points | 26 to 45 | |
| 17 |
Alloy Composition
| Boron (B), % | 0 to 0.1 | |
| 0 |
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.060 |
| Chromium (Cr), % | 19 to 21 | |
| 19 to 21.5 |
| Cobalt (Co), % | 39 to 41 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.75 |
| Iron (Fe), % | 10 to 20.5 | |
| 58.6 to 67.4 |
| Manganese (Mn), % | 1.5 to 2.5 | |
| 8.0 to 10 |
| Molybdenum (Mo), % | 6.0 to 8.0 | |
| 0 to 0.75 |
| Nickel (Ni), % | 14 to 16 | |
| 5.5 to 7.0 |
| Nitrogen (N), % | 0 | |
| 0.1 to 0.3 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.2 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |