R30006 Cobalt vs. 772.0 Aluminum

R30006 cobalt belongs to the cobalt alloys classification, while 772.0 aluminum belongs to the aluminum alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is R30006 cobalt and the bottom bar is 772.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
69
Elongation at Break, % 1.0
6.3 to 8.4
Fatigue Strength, MPa 260
94 to 160
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 85
26
Tensile Strength: Ultimate (UTS), MPa 900
260 to 320
Tensile Strength: Yield (Proof), MPa 540
220 to 250

Thermal Properties

Latent Heat of Fusion, J/g 320
380
Melting Completion (Liquidus), °C 1400
630
Melting Onset (Solidus), °C 1290
580
Specific Heat Capacity, J/kg-K 450
870
Thermal Conductivity, W/m-K 15
150
Thermal Expansion, µm/m-K 11
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.6
35
Electrical Conductivity: Equal Weight (Specific), % IACS 1.7
110

Otherwise Unclassified Properties

Density, g/cm3 8.6
3.0
Embodied Carbon, kg CO2/kg material 7.8
8.0
Embodied Energy, MJ/kg 110
150
Embodied Water, L/kg 500
1140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 7.8
16 to 25
Resilience: Unit (Modulus of Resilience), kJ/m3 670
350 to 430
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
46
Strength to Weight: Axial, points 29
25 to 31
Strength to Weight: Bending, points 24
31 to 36
Thermal Diffusivity, mm2/s 3.9
58
Thermal Shock Resistance, points 26
11 to 14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
91.2 to 93.2
Carbon (C), % 0.9 to 1.4
0
Chromium (Cr), % 27 to 32
0.060 to 0.2
Cobalt (Co), % 48.6 to 68.1
0
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 0 to 3.0
0 to 0.15
Magnesium (Mg), % 0
0.6 to 0.8
Manganese (Mn), % 0
0 to 0.1
Molybdenum (Mo), % 0 to 1.0
0
Nickel (Ni), % 0 to 3.0
0
Silicon (Si), % 0 to 2.0
0 to 0.15
Titanium (Ti), % 0
0.1 to 0.2
Tungsten (W), % 4.0 to 6.0
0
Zinc (Zn), % 0
6.0 to 7.0
Residuals, % 0
0 to 0.15