R30006 cobalt belongs to the cobalt alloys classification, while EN 1.4376 stainless steel belongs to the iron alloys. They have a modest 22% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is R30006 cobalt and the bottom bar is EN 1.4376 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 1.0
45
Fatigue Strength, MPa 260
420
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 85
77
Tensile Strength: Ultimate (UTS), MPa 900
750
Tensile Strength: Yield (Proof), MPa 540
450

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Melting Completion (Liquidus), °C 1400
1410
Melting Onset (Solidus), °C 1290
1370
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 11
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.6
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.7
2.8

Otherwise Unclassified Properties

Density, g/cm3 8.6
7.7
Embodied Carbon, kg CO2/kg material 7.8
2.6
Embodied Energy, MJ/kg 110
37
Embodied Water, L/kg 500
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 7.8
290
Resilience: Unit (Modulus of Resilience), kJ/m3 670
520
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 29
27
Strength to Weight: Bending, points 24
24
Thermal Diffusivity, mm2/s 3.9
4.0
Thermal Shock Resistance, points 26
17

Alloy Composition

Carbon (C), % 0.9 to 1.4
0 to 0.1
Chromium (Cr), % 27 to 32
17 to 20.5
Cobalt (Co), % 48.6 to 68.1
0
Iron (Fe), % 0 to 3.0
65.5 to 76
Manganese (Mn), % 0
5.0 to 8.0
Molybdenum (Mo), % 0 to 1.0
0
Nickel (Ni), % 0 to 3.0
2.0 to 4.5
Nitrogen (N), % 0
0 to 0.3
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Tungsten (W), % 4.0 to 6.0
0