R30006 Cobalt vs. EN 1.6308 Steel

R30006 cobalt belongs to the cobalt alloys classification, while EN 1.6308 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is R30006 cobalt and the bottom bar is EN 1.6308 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 1.0
23
Fatigue Strength, MPa 260
320
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 85
73
Tensile Strength: Ultimate (UTS), MPa 900
610
Tensile Strength: Yield (Proof), MPa 540
460

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1290
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 15
39
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.6
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.7
8.4

Otherwise Unclassified Properties

Density, g/cm3 8.6
7.9
Embodied Carbon, kg CO2/kg material 7.8
1.6
Embodied Energy, MJ/kg 110
22
Embodied Water, L/kg 500
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 7.8
130
Resilience: Unit (Modulus of Resilience), kJ/m3 670
550
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 29
22
Strength to Weight: Bending, points 24
20
Thermal Diffusivity, mm2/s 3.9
10
Thermal Shock Resistance, points 26
18

Alloy Composition

Carbon (C), % 0.9 to 1.4
0 to 0.2
Chromium (Cr), % 27 to 32
0
Cobalt (Co), % 48.6 to 68.1
0
Iron (Fe), % 0 to 3.0
96.4 to 97.9
Manganese (Mn), % 0
1.2 to 1.6
Molybdenum (Mo), % 0 to 1.0
0.45 to 0.55
Nickel (Ni), % 0 to 3.0
0.5 to 0.8
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 2.0
0 to 0.4
Sulfur (S), % 0
0 to 0.015
Tungsten (W), % 4.0 to 6.0
0
Vanadium (V), % 0
0 to 0.030