R30006 Cobalt vs. CC760S Brass

R30006 cobalt belongs to the cobalt alloys classification, while CC760S brass belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is R30006 cobalt and the bottom bar is CC760S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
110
Elongation at Break, % 1.0
22
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 85
42
Tensile Strength: Ultimate (UTS), MPa 900
180
Tensile Strength: Yield (Proof), MPa 540
80

Thermal Properties

Latent Heat of Fusion, J/g 320
190
Melting Completion (Liquidus), °C 1400
1000
Melting Onset (Solidus), °C 1290
940
Specific Heat Capacity, J/kg-K 450
390
Thermal Conductivity, W/m-K 15
150
Thermal Expansion, µm/m-K 11
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.6
38
Electrical Conductivity: Equal Weight (Specific), % IACS 1.7
40

Otherwise Unclassified Properties

Density, g/cm3 8.6
8.6
Embodied Carbon, kg CO2/kg material 7.8
2.6
Embodied Energy, MJ/kg 110
43
Embodied Water, L/kg 500
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 7.8
33
Resilience: Unit (Modulus of Resilience), kJ/m3 670
29
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 23
19
Strength to Weight: Axial, points 29
5.8
Strength to Weight: Bending, points 24
8.2
Thermal Diffusivity, mm2/s 3.9
45
Thermal Shock Resistance, points 26
6.2

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Arsenic (As), % 0
0.050 to 0.15
Carbon (C), % 0.9 to 1.4
0
Chromium (Cr), % 27 to 32
0
Cobalt (Co), % 48.6 to 68.1
0
Copper (Cu), % 0
83 to 88
Iron (Fe), % 0 to 3.0
0 to 0.15
Lead (Pb), % 0
0 to 0.5
Manganese (Mn), % 0
0 to 0.1
Molybdenum (Mo), % 0 to 1.0
0
Nickel (Ni), % 0 to 3.0
0 to 0.1
Silicon (Si), % 0 to 2.0
0 to 0.020
Tin (Sn), % 0
0 to 0.3
Tungsten (W), % 4.0 to 6.0
0
Zinc (Zn), % 0
10.7 to 17