R30006 Cobalt vs. Solder Alloy 704

R30006 cobalt belongs to the cobalt alloys classification, while solder alloy 704 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is R30006 cobalt and the bottom bar is solder alloy 704.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
51
Elongation at Break, % 1.0
30
Poisson's Ratio 0.28
0.36
Shear Modulus, GPa 85
19
Tensile Strength: Ultimate (UTS), MPa 900
55

Thermal Properties

Latent Heat of Fusion, J/g 320
62
Melting Completion (Liquidus), °C 1400
240
Melting Onset (Solidus), °C 1290
220
Specific Heat Capacity, J/kg-K 450
220
Thermal Conductivity, W/m-K 15
50
Thermal Expansion, µm/m-K 11
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.6
13
Electrical Conductivity: Equal Weight (Specific), % IACS 1.7
15

Otherwise Unclassified Properties

Density, g/cm3 8.6
7.5
Embodied Carbon, kg CO2/kg material 7.8
19
Embodied Energy, MJ/kg 110
320

Common Calculations

Stiffness to Weight: Axial, points 14
3.8
Stiffness to Weight: Bending, points 23
17
Strength to Weight: Axial, points 29
2.1
Strength to Weight: Bending, points 24
4.3
Thermal Diffusivity, mm2/s 3.9
30
Thermal Shock Resistance, points 26
3.5

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0.9 to 1.4
0
Chromium (Cr), % 27 to 32
0
Cobalt (Co), % 48.6 to 68.1
0
Copper (Cu), % 0
0 to 0.050
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 3.0
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Molybdenum (Mo), % 0 to 1.0
0
Nickel (Ni), % 0 to 3.0
0 to 0.010
Silicon (Si), % 0 to 2.0
0
Silver (Ag), % 0
4.8 to 5.2
Tin (Sn), % 0
94.3 to 95.2
Tungsten (W), % 4.0 to 6.0
0
Zinc (Zn), % 0
0 to 0.0010