R30008 Cobalt vs. ASTM A732 Cast Steel
R30008 cobalt belongs to the cobalt alloys classification, while ASTM A732 cast steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is R30008 cobalt and the bottom bar is ASTM A732 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 1.1 to 73 | |
| 4.0 to 25 |
| Fatigue Strength, MPa | 320 to 530 | |
| 230 to 750 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 83 | |
| 72 to 73 |
| Tensile Strength: Ultimate (UTS), MPa | 950 to 1700 | |
| 460 to 1470 |
| Tensile Strength: Yield (Proof), MPa | 500 to 1080 | |
| 310 to 1340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 250 to 260 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1440 to 1460 |
| Melting Onset (Solidus), °C | 1330 | |
| 1400 to 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 to 480 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 95 | |
| 2.0 to 3.8 |
| Density, g/cm3 | 8.4 | |
| 7.8 to 7.9 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 1.4 to 1.7 |
| Embodied Energy, MJ/kg | 110 | |
| 19 to 24 |
| Embodied Water, L/kg | 400 | |
| 47 to 54 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 590 to 2720 | |
| 260 to 4770 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 31 to 56 | |
| 16 to 52 |
| Strength to Weight: Bending, points | 25 to 37 | |
| 17 to 37 |
| Thermal Shock Resistance, points | 25 to 44 | |
| 14 to 43 |