R30008 Cobalt vs. EN 1.7216 Steel
R30008 cobalt belongs to the cobalt alloys classification, while EN 1.7216 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is R30008 cobalt and the bottom bar is EN 1.7216 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 210 | |
190 |
Elongation at Break, % | 1.1 to 73 | |
12 to 23 |
Fatigue Strength, MPa | 320 to 530 | |
290 to 440 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 83 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 950 to 1700 | |
650 to 930 |
Tensile Strength: Yield (Proof), MPa | 500 to 1080 | |
400 to 690 |
Thermal Properties
Latent Heat of Fusion, J/g | 320 | |
250 |
Melting Completion (Liquidus), °C | 1400 | |
1460 |
Melting Onset (Solidus), °C | 1330 | |
1420 |
Specific Heat Capacity, J/kg-K | 450 | |
470 |
Thermal Expansion, µm/m-K | 13 | |
13 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 95 | |
2.4 |
Density, g/cm3 | 8.4 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 8.1 | |
1.5 |
Embodied Energy, MJ/kg | 110 | |
20 |
Embodied Water, L/kg | 400 | |
50 |
Common Calculations
Resilience: Unit (Modulus of Resilience), kJ/m3 | 590 to 2720 | |
430 to 1280 |
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 31 to 56 | |
23 to 33 |
Strength to Weight: Bending, points | 25 to 37 | |
21 to 27 |
Thermal Shock Resistance, points | 25 to 44 | |
19 to 27 |
Alloy Composition
Boron (B), % | 0 to 0.0010 | |
0 |
Carbon (C), % | 0 to 0.15 | |
0.27 to 0.34 |
Chromium (Cr), % | 18.5 to 21.5 | |
0.8 to 1.2 |
Cobalt (Co), % | 39 to 42 | |
0 |
Iron (Fe), % | 7.6 to 20 | |
97.2 to 98.4 |
Manganese (Mn), % | 1.0 to 2.0 | |
0.35 to 0.6 |
Molybdenum (Mo), % | 6.5 to 7.5 | |
0.15 to 0.3 |
Nickel (Ni), % | 15 to 18 | |
0 |
Phosphorus (P), % | 0 to 0.015 | |
0 to 0.035 |
Silicon (Si), % | 0 to 1.2 | |
0 to 0.35 |
Sulfur (S), % | 0 to 0.015 | |
0 to 0.035 |