R30016 Cobalt vs. EN 1.1203 Steel
R30016 cobalt belongs to the cobalt alloys classification, while EN 1.1203 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is R30016 cobalt and the bottom bar is EN 1.1203 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 8.4 | |
| 12 to 15 |
| Fatigue Strength, MPa | 290 | |
| 210 to 310 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 85 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 1010 | |
| 690 to 780 |
| Tensile Strength: Yield (Proof), MPa | 580 | |
| 340 to 480 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 250 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1460 |
| Melting Onset (Solidus), °C | 1270 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 15 | |
| 48 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.9 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.0 | |
| 8.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 7.7 | |
| 1.4 |
| Embodied Energy, MJ/kg | 110 | |
| 19 |
| Embodied Water, L/kg | 500 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 72 | |
| 69 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 770 | |
| 310 to 610 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 33 | |
| 25 to 28 |
| Strength to Weight: Bending, points | 26 | |
| 22 to 24 |
| Thermal Diffusivity, mm2/s | 3.9 | |
| 13 |
| Thermal Shock Resistance, points | 24 | |
| 22 to 25 |
Alloy Composition
| Carbon (C), % | 0.9 to 1.4 | |
| 0.52 to 0.6 |
| Chromium (Cr), % | 28 to 32 | |
| 0 to 0.4 |
| Cobalt (Co), % | 49.6 to 66.9 | |
| 0 |
| Iron (Fe), % | 0 to 3.0 | |
| 97.1 to 98.9 |
| Manganese (Mn), % | 0.5 to 2.0 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 0 to 1.5 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 to 3.0 | |
| 0 to 0.4 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Silicon (Si), % | 0.2 to 2.0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.035 |
| Tungsten (W), % | 3.5 to 5.5 | |
| 0 |