R30021 Cobalt vs. ACI-ASTM CB30 Steel

R30021 cobalt belongs to the cobalt alloys classification, while ACI-ASTM CB30 steel belongs to the iron alloys. They have a modest 23% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is R30021 cobalt and the bottom bar is ACI-ASTM CB30 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 86
77
Tensile Strength: Ultimate (UTS), MPa 700
500
Tensile Strength: Yield (Proof), MPa 500
230

Thermal Properties

Latent Heat of Fusion, J/g 330
290
Melting Completion (Liquidus), °C 1350
1430
Melting Onset (Solidus), °C 1190
1380
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 15
21
Thermal Expansion, µm/m-K 11
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
3.0

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.7
Embodied Carbon, kg CO2/kg material 8.0
2.3
Embodied Energy, MJ/kg 110
33
Embodied Water, L/kg 520
130

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 570
140
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23
18
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 3.8
5.6
Thermal Shock Resistance, points 21
17

Alloy Composition

Carbon (C), % 0.2 to 0.35
0 to 0.3
Chromium (Cr), % 26 to 29
18 to 21
Cobalt (Co), % 61.7 to 67.3
0
Copper (Cu), % 0
0 to 1.2
Iron (Fe), % 0 to 3.0
72.9 to 82
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 4.5 to 6.0
0
Nickel (Ni), % 2.0 to 3.0
0 to 2.0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.5
Sulfur (S), % 0
0 to 0.040