R30021 Cobalt vs. EN 1.0215 Steel

R30021 cobalt belongs to the cobalt alloys classification, while EN 1.0215 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is R30021 cobalt and the bottom bar is EN 1.0215 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 9.0
25
Fatigue Strength, MPa 250
180
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 86
73
Tensile Strength: Ultimate (UTS), MPa 700
350
Tensile Strength: Yield (Proof), MPa 500
250

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Melting Completion (Liquidus), °C 1350
1460
Melting Onset (Solidus), °C 1190
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 15
53
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
8.0

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.9
Embodied Carbon, kg CO2/kg material 8.0
1.4
Embodied Energy, MJ/kg 110
18
Embodied Water, L/kg 520
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 57
79
Resilience: Unit (Modulus of Resilience), kJ/m3 570
160
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
13
Strength to Weight: Bending, points 21
14
Thermal Diffusivity, mm2/s 3.8
14
Thermal Shock Resistance, points 21
11

Alloy Composition

Carbon (C), % 0.2 to 0.35
0 to 0.14
Chromium (Cr), % 26 to 29
0
Cobalt (Co), % 61.7 to 67.3
0
Iron (Fe), % 0 to 3.0
98.7 to 100
Manganese (Mn), % 0
0 to 0.7
Molybdenum (Mo), % 4.5 to 6.0
0
Nickel (Ni), % 2.0 to 3.0
0
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 1.5
0 to 0.35
Sulfur (S), % 0
0 to 0.045