R30021 Cobalt vs. EN 1.3567 Steel

R30021 cobalt belongs to the cobalt alloys classification, while EN 1.3567 steel belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is R30021 cobalt and the bottom bar is EN 1.3567 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 86
73
Tensile Strength: Ultimate (UTS), MPa 700
500 to 1420

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Melting Completion (Liquidus), °C 1350
1460
Melting Onset (Solidus), °C 1190
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 15
45
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
8.3

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 8.0
1.5
Embodied Energy, MJ/kg 110
20
Embodied Water, L/kg 520
52

Common Calculations

Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
18 to 50
Strength to Weight: Bending, points 21
18 to 36
Thermal Diffusivity, mm2/s 3.8
12
Thermal Shock Resistance, points 21
15 to 42

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0.2 to 0.35
0.17 to 0.23
Chromium (Cr), % 26 to 29
0.9 to 1.2
Cobalt (Co), % 61.7 to 67.3
0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 0 to 3.0
96.8 to 98.4
Manganese (Mn), % 0
0.6 to 0.9
Molybdenum (Mo), % 4.5 to 6.0
0.15 to 0.25
Nickel (Ni), % 2.0 to 3.0
0
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 1.5
0 to 0.4
Sulfur (S), % 0
0 to 0.030