R30021 Cobalt vs. EN 1.4107 Stainless Steel

R30021 cobalt belongs to the cobalt alloys classification, while EN 1.4107 stainless steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is R30021 cobalt and the bottom bar is EN 1.4107 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 9.0
18 to 21
Fatigue Strength, MPa 250
260 to 350
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 86
76
Tensile Strength: Ultimate (UTS), MPa 700
620 to 700
Tensile Strength: Yield (Proof), MPa 500
400 to 570

Thermal Properties

Latent Heat of Fusion, J/g 330
270
Melting Completion (Liquidus), °C 1350
1450
Melting Onset (Solidus), °C 1190
1410
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 15
27
Thermal Expansion, µm/m-K 11
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
3.3

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 8.0
2.1
Embodied Energy, MJ/kg 110
30
Embodied Water, L/kg 520
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 57
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 570
420 to 840
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23
22 to 25
Strength to Weight: Bending, points 21
21 to 22
Thermal Diffusivity, mm2/s 3.8
7.2
Thermal Shock Resistance, points 21
22 to 25

Alloy Composition

Carbon (C), % 0.2 to 0.35
0 to 0.1
Chromium (Cr), % 26 to 29
11.5 to 12.5
Cobalt (Co), % 61.7 to 67.3
0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 0 to 3.0
83.8 to 87.2
Manganese (Mn), % 0
0.5 to 0.8
Molybdenum (Mo), % 4.5 to 6.0
0 to 0.5
Nickel (Ni), % 2.0 to 3.0
0.8 to 1.5
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 1.5
0 to 0.4
Sulfur (S), % 0
0 to 0.020
Vanadium (V), % 0
0 to 0.080