R30021 Cobalt vs. EN 1.4405 Stainless Steel

R30021 cobalt belongs to the cobalt alloys classification, while EN 1.4405 stainless steel belongs to the iron alloys. They have a modest 22% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is R30021 cobalt and the bottom bar is EN 1.4405 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 9.0
17
Fatigue Strength, MPa 250
370
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 86
77
Tensile Strength: Ultimate (UTS), MPa 700
860
Tensile Strength: Yield (Proof), MPa 500
610

Thermal Properties

Latent Heat of Fusion, J/g 330
280
Melting Completion (Liquidus), °C 1350
1450
Melting Onset (Solidus), °C 1190
1400
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 15
17
Thermal Expansion, µm/m-K 11
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
2.5

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 8.0
2.8
Embodied Energy, MJ/kg 110
39
Embodied Water, L/kg 520
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 57
130
Resilience: Unit (Modulus of Resilience), kJ/m3 570
950
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23
31
Strength to Weight: Bending, points 21
26
Thermal Diffusivity, mm2/s 3.8
4.6
Thermal Shock Resistance, points 21
29

Alloy Composition

Carbon (C), % 0.2 to 0.35
0 to 0.060
Chromium (Cr), % 26 to 29
15 to 17
Cobalt (Co), % 61.7 to 67.3
0
Iron (Fe), % 0 to 3.0
73.6 to 80.3
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 4.5 to 6.0
0.7 to 1.5
Nickel (Ni), % 2.0 to 3.0
4.0 to 6.0
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 1.5
0 to 0.8
Sulfur (S), % 0
0 to 0.025