R30021 Cobalt vs. EN AC-44300 Aluminum

R30021 cobalt belongs to the cobalt alloys classification, while EN AC-44300 aluminum belongs to the aluminum alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is R30021 cobalt and the bottom bar is EN AC-44300 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
72
Elongation at Break, % 9.0
1.1
Fatigue Strength, MPa 250
100
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 86
27
Tensile Strength: Ultimate (UTS), MPa 700
270
Tensile Strength: Yield (Proof), MPa 500
150

Thermal Properties

Latent Heat of Fusion, J/g 330
570
Melting Completion (Liquidus), °C 1350
590
Melting Onset (Solidus), °C 1190
580
Specific Heat Capacity, J/kg-K 450
900
Thermal Conductivity, W/m-K 15
130
Thermal Expansion, µm/m-K 11
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
33
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
120

Otherwise Unclassified Properties

Density, g/cm3 8.4
2.5
Embodied Carbon, kg CO2/kg material 8.0
7.7
Embodied Energy, MJ/kg 110
140
Embodied Water, L/kg 520
1050

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 57
2.6
Resilience: Unit (Modulus of Resilience), kJ/m3 570
150
Stiffness to Weight: Axial, points 15
16
Stiffness to Weight: Bending, points 24
55
Strength to Weight: Axial, points 23
29
Strength to Weight: Bending, points 21
36
Thermal Diffusivity, mm2/s 3.8
58
Thermal Shock Resistance, points 21
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
84.3 to 89.5
Carbon (C), % 0.2 to 0.35
0
Chromium (Cr), % 26 to 29
0
Cobalt (Co), % 61.7 to 67.3
0
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 0 to 3.0
0 to 1.0
Manganese (Mn), % 0
0 to 0.55
Molybdenum (Mo), % 4.5 to 6.0
0
Nickel (Ni), % 2.0 to 3.0
0
Silicon (Si), % 0 to 1.5
10.5 to 13.5
Titanium (Ti), % 0
0 to 0.15
Zinc (Zn), % 0
0 to 0.15
Residuals, % 0
0 to 0.25