R30021 Cobalt vs. SAE-AISI M10 Steel

R30021 cobalt belongs to the cobalt alloys classification, while SAE-AISI M10 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is R30021 cobalt and the bottom bar is SAE-AISI M10 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 86
76
Tensile Strength: Ultimate (UTS), MPa 700
740 to 2170

Thermal Properties

Latent Heat of Fusion, J/g 330
270
Melting Completion (Liquidus), °C 1350
1520
Melting Onset (Solidus), °C 1190
1470
Specific Heat Capacity, J/kg-K 450
460
Thermal Conductivity, W/m-K 15
31
Thermal Expansion, µm/m-K 11
12

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.9
Embodied Carbon, kg CO2/kg material 8.0
8.3
Embodied Energy, MJ/kg 110
120
Embodied Water, L/kg 520
100

Common Calculations

Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
26 to 76
Strength to Weight: Bending, points 21
23 to 47
Thermal Diffusivity, mm2/s 3.8
8.5
Thermal Shock Resistance, points 21
23 to 68

Alloy Composition

Carbon (C), % 0.2 to 0.35
0.84 to 1.1
Chromium (Cr), % 26 to 29
3.8 to 4.5
Cobalt (Co), % 61.7 to 67.3
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 0 to 3.0
82.3 to 85.6
Manganese (Mn), % 0
0.1 to 0.4
Molybdenum (Mo), % 4.5 to 6.0
7.8 to 8.5
Nickel (Ni), % 2.0 to 3.0
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 1.5
0.2 to 0.45
Sulfur (S), % 0
0 to 0.030
Vanadium (V), % 0
1.8 to 2.2