R30021 Cobalt vs. S31060 Stainless Steel

R30021 cobalt belongs to the cobalt alloys classification, while S31060 stainless steel belongs to the iron alloys. They have a modest 27% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is R30021 cobalt and the bottom bar is S31060 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 9.0
46
Fatigue Strength, MPa 250
290
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 86
78
Tensile Strength: Ultimate (UTS), MPa 700
680
Tensile Strength: Yield (Proof), MPa 500
310

Thermal Properties

Latent Heat of Fusion, J/g 330
290
Melting Completion (Liquidus), °C 1350
1420
Melting Onset (Solidus), °C 1190
1370
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 11
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
2.4

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 8.0
3.4
Embodied Energy, MJ/kg 110
48
Embodied Water, L/kg 520
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 57
260
Resilience: Unit (Modulus of Resilience), kJ/m3 570
250
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23
24
Strength to Weight: Bending, points 21
22
Thermal Diffusivity, mm2/s 3.8
4.0
Thermal Shock Resistance, points 21
15

Alloy Composition

Boron (B), % 0
0.0010 to 0.010
Carbon (C), % 0.2 to 0.35
0.050 to 0.1
Cerium (Ce), % 0
0 to 0.070
Chromium (Cr), % 26 to 29
22 to 24
Cobalt (Co), % 61.7 to 67.3
0
Iron (Fe), % 0 to 3.0
61.4 to 67.8
Lanthanum (La), % 0
0 to 0.070
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 4.5 to 6.0
0
Nickel (Ni), % 2.0 to 3.0
10 to 12.5
Nitrogen (N), % 0
0.18 to 0.25
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 0.5
Sulfur (S), % 0
0 to 0.030