R30035 Cobalt vs. ASTM B631 Class A
R30035 cobalt belongs to the cobalt alloys classification, while ASTM B631 class A belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is R30035 cobalt and the bottom bar is ASTM B631 class A.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 to 230 | |
| 220 |
| Poisson's Ratio | 0.29 | |
| 0.3 |
| Shear Modulus, GPa | 84 to 89 | |
| 85 to 86 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 160 |
| Melting Completion (Liquidus), °C | 1440 | |
| 2680 to 2690 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 160 |
| Thermal Conductivity, W/m-K | 11 | |
| 420 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.7 | |
| 40 to 47 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.8 | |
| 25 to 29 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.7 | |
| 15 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 43 |
| Embodied Energy, MJ/kg | 140 | |
| 670 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 to 15 | |
| 8.5 |
| Stiffness to Weight: Bending, points | 23 to 24 | |
| 14 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 180 |