R30816 Cobalt vs. AISI 416Se Stainless Steel
R30816 cobalt belongs to the cobalt alloys classification, while AISI 416Se stainless steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is R30816 cobalt and the bottom bar is AISI 416Se stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 280 | |
| 230 |
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 23 | |
| 23 |
| Fatigue Strength, MPa | 250 | |
| 210 |
| Poisson's Ratio | 0.3 | |
| 0.28 |
| Reduction in Area, % | 22 | |
| 50 |
| Shear Modulus, GPa | 81 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 1020 | |
| 540 |
| Tensile Strength: Yield (Proof), MPa | 460 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 270 |
| Melting Completion (Liquidus), °C | 1540 | |
| 1440 |
| Melting Onset (Solidus), °C | 1460 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 480 |
| Thermal Conductivity, W/m-K | 13 | |
| 30 |
| Thermal Expansion, µm/m-K | 12 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.1 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 20 | |
| 1.9 |
| Embodied Energy, MJ/kg | 320 | |
| 27 |
| Embodied Water, L/kg | 440 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 510 | |
| 250 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 22 | |
| 25 |
| Strength to Weight: Axial, points | 31 | |
| 20 |
| Strength to Weight: Bending, points | 25 | |
| 19 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 8.1 |
| Thermal Shock Resistance, points | 28 | |
| 20 |
Alloy Composition
| Carbon (C), % | 0.32 to 0.42 | |
| 0 to 0.15 |
| Chromium (Cr), % | 19 to 21 | |
| 12 to 14 |
| Cobalt (Co), % | 40 to 49.8 | |
| 0 |
| Iron (Fe), % | 0 to 5.0 | |
| 83.1 to 87.9 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 0 to 1.3 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0 |
| Nickel (Ni), % | 19 to 21 | |
| 0 |
| Niobium (Nb), % | 3.5 to 4.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.060 |
| Selenium (Se), % | 0 | |
| 0.15 to 0.35 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.060 |
| Tantalum (Ta), % | 3.5 to 4.5 | |
| 0 |
| Tungsten (W), % | 3.5 to 4.5 | |
| 0 |