R58150 Titanium vs. 5050 Aluminum
R58150 titanium belongs to the titanium alloys classification, while 5050 aluminum belongs to the aluminum alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is R58150 titanium and the bottom bar is 5050 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 68 |
| Elongation at Break, % | 13 | |
| 1.7 to 22 |
| Fatigue Strength, MPa | 330 | |
| 45 to 100 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 52 | |
| 26 |
| Shear Strength, MPa | 470 | |
| 91 to 140 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 140 to 250 |
| Tensile Strength: Yield (Proof), MPa | 550 | |
| 50 to 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 180 |
| Melting Completion (Liquidus), °C | 1760 | |
| 650 |
| Melting Onset (Solidus), °C | 1700 | |
| 630 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 900 |
| Thermal Expansion, µm/m-K | 8.4 | |
| 24 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 48 | |
| 9.5 |
| Density, g/cm3 | 5.4 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 31 | |
| 8.4 |
| Embodied Energy, MJ/kg | 480 | |
| 150 |
| Embodied Water, L/kg | 150 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 94 | |
| 4.1 to 24 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1110 | |
| 18 to 330 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 32 | |
| 50 |
| Strength to Weight: Axial, points | 40 | |
| 15 to 26 |
| Strength to Weight: Bending, points | 35 | |
| 22 to 33 |
| Thermal Shock Resistance, points | 48 | |
| 6.3 to 11 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 96.3 to 98.9 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 | |
| 0 to 0.2 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 0 | |
| 1.1 to 1.8 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 14 to 16 | |
| 0 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 |
| Oxygen (O), % | 0 to 0.2 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.4 |
| Titanium (Ti), % | 83.5 to 86 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |