R58150 Titanium vs. 6262 Aluminum
R58150 titanium belongs to the titanium alloys classification, while 6262 aluminum belongs to the aluminum alloys. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is R58150 titanium and the bottom bar is 6262 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 68 |
| Elongation at Break, % | 13 | |
| 4.6 to 10 |
| Fatigue Strength, MPa | 330 | |
| 90 to 110 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 52 | |
| 26 |
| Shear Strength, MPa | 470 | |
| 170 to 240 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 290 to 390 |
| Tensile Strength: Yield (Proof), MPa | 550 | |
| 270 to 360 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 160 |
| Melting Completion (Liquidus), °C | 1760 | |
| 650 |
| Melting Onset (Solidus), °C | 1700 | |
| 580 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 890 |
| Thermal Expansion, µm/m-K | 8.4 | |
| 23 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 48 | |
| 10 |
| Density, g/cm3 | 5.4 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 31 | |
| 8.3 |
| Embodied Energy, MJ/kg | 480 | |
| 150 |
| Embodied Water, L/kg | 150 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 94 | |
| 17 to 31 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1110 | |
| 530 to 940 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 32 | |
| 48 |
| Strength to Weight: Axial, points | 40 | |
| 29 to 39 |
| Strength to Weight: Bending, points | 35 | |
| 35 to 42 |
| Thermal Shock Resistance, points | 48 | |
| 13 to 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 94.7 to 97.8 |
| Bismuth (Bi), % | 0 | |
| 0.4 to 0.7 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.040 to 0.14 |
| Copper (Cu), % | 0 | |
| 0.15 to 0.4 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.7 |
| Lead (Pb), % | 0 | |
| 0.4 to 0.7 |
| Magnesium (Mg), % | 0 | |
| 0.8 to 1.2 |
| Manganese (Mn), % | 0 | |
| 0 to 0.15 |
| Molybdenum (Mo), % | 14 to 16 | |
| 0 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 |
| Oxygen (O), % | 0 to 0.2 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0.4 to 0.8 |
| Titanium (Ti), % | 83.5 to 86 | |
| 0 to 0.15 |
| Zinc (Zn), % | 0 | |
| 0 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |