R58150 Titanium vs. Grade 29 Titanium
Both R58150 titanium and grade 29 titanium are titanium alloys. They have 85% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is R58150 titanium and the bottom bar is grade 29 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 110 |
| Elongation at Break, % | 13 | |
| 6.8 to 11 |
| Fatigue Strength, MPa | 330 | |
| 460 to 510 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Reduction in Area, % | 68 | |
| 17 |
| Shear Modulus, GPa | 52 | |
| 40 |
| Shear Strength, MPa | 470 | |
| 550 to 560 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 930 to 940 |
| Tensile Strength: Yield (Proof), MPa | 550 | |
| 850 to 870 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 340 |
| Melting Completion (Liquidus), °C | 1760 | |
| 1610 |
| Melting Onset (Solidus), °C | 1700 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 560 |
| Thermal Expansion, µm/m-K | 8.4 | |
| 9.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 48 | |
| 36 |
| Density, g/cm3 | 5.4 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 31 | |
| 39 |
| Embodied Energy, MJ/kg | 480 | |
| 640 |
| Embodied Water, L/kg | 150 | |
| 410 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 94 | |
| 62 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1110 | |
| 3420 to 3540 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 32 | |
| 35 |
| Strength to Weight: Axial, points | 40 | |
| 58 to 59 |
| Strength to Weight: Bending, points | 35 | |
| 47 to 48 |
| Thermal Shock Resistance, points | 48 | |
| 68 to 69 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 5.5 to 6.5 |
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.080 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.25 |
| Molybdenum (Mo), % | 14 to 16 | |
| 0 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 to 0.2 | |
| 0 to 0.13 |
| Ruthenium (Ru), % | 0 | |
| 0.080 to 0.14 |
| Titanium (Ti), % | 83.5 to 86 | |
| 88 to 90.9 |
| Vanadium (V), % | 0 | |
| 3.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |