R60705 Alloy vs. AISI 310HCb Stainless Steel

R60705 alloy belongs to the otherwise unclassified metals classification, while AISI 310HCb stainless steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is R60705 alloy and the bottom bar is AISI 310HCb stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
200
Elongation at Break, % 18
46
Fatigue Strength, MPa 290
210
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 37
78
Tensile Strength: Ultimate (UTS), MPa 540
590
Tensile Strength: Yield (Proof), MPa 430
230

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Specific Heat Capacity, J/kg-K 270
480
Thermal Conductivity, W/m-K 17
15
Thermal Expansion, µm/m-K 6.3
16

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.9
Embodied Water, L/kg 450
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
210
Resilience: Unit (Modulus of Resilience), kJ/m3 950
130
Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 9.5
3.9
Thermal Shock Resistance, points 63
13

Alloy Composition

Carbon (C), % 0 to 0.050
0.040 to 0.1
Chromium (Cr), % 0 to 0.2
24 to 26
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
48 to 57
Manganese (Mn), % 0
0 to 2.0
Nickel (Ni), % 0
19 to 22
Niobium (Nb), % 2.0 to 3.0
0 to 1.1
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.18
0
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0
0 to 0.75
Sulfur (S), % 0
0 to 0.030
Zirconium (Zr), % 91 to 98
0