R60705 Alloy vs. AISI 416Se Stainless Steel

R60705 alloy belongs to the otherwise unclassified metals classification, while AISI 416Se stainless steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is R60705 alloy and the bottom bar is AISI 416Se stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
190
Elongation at Break, % 18
23
Fatigue Strength, MPa 290
210
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 37
76
Tensile Strength: Ultimate (UTS), MPa 540
540
Tensile Strength: Yield (Proof), MPa 430
310

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Specific Heat Capacity, J/kg-K 270
480
Thermal Conductivity, W/m-K 17
30
Thermal Expansion, µm/m-K 6.3
10

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.7
Embodied Water, L/kg 450
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
110
Resilience: Unit (Modulus of Resilience), kJ/m3 950
250
Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 22
20
Strength to Weight: Bending, points 22
19
Thermal Diffusivity, mm2/s 9.5
8.1
Thermal Shock Resistance, points 63
20

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.15
Chromium (Cr), % 0 to 0.2
12 to 14
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
83.1 to 87.9
Manganese (Mn), % 0
0 to 1.3
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.18
0
Phosphorus (P), % 0
0 to 0.060
Selenium (Se), % 0
0.15 to 0.35
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.060
Zirconium (Zr), % 91 to 98
0