R60705 Alloy vs. EN 1.3967 Stainless Steel

R60705 alloy belongs to the otherwise unclassified metals classification, while EN 1.3967 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is R60705 alloy and the bottom bar is EN 1.3967 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
200
Elongation at Break, % 18
22
Fatigue Strength, MPa 290
240
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 37
79
Tensile Strength: Ultimate (UTS), MPa 540
690
Tensile Strength: Yield (Proof), MPa 430
350

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Specific Heat Capacity, J/kg-K 270
470
Thermal Expansion, µm/m-K 6.3
16

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.9
Embodied Water, L/kg 450
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
130
Resilience: Unit (Modulus of Resilience), kJ/m3 950
310
Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 22
24
Strength to Weight: Bending, points 22
22
Thermal Shock Resistance, points 63
15

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.030
Chromium (Cr), % 0 to 0.2
20 to 21.5
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
50.3 to 57.8
Manganese (Mn), % 0
4.0 to 6.0
Molybdenum (Mo), % 0
3.0 to 3.5
Nickel (Ni), % 0
15 to 17
Niobium (Nb), % 2.0 to 3.0
0 to 0.25
Nitrogen (N), % 0 to 0.025
0.2 to 0.35
Oxygen (O), % 0 to 0.18
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.010
Zirconium (Zr), % 91 to 98
0