MakeItFrom.com
Menu (ESC)

R60705 Alloy vs. EN 1.4598 Stainless Steel

R60705 alloy belongs to the otherwise unclassified metals classification, while EN 1.4598 stainless steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is R60705 alloy and the bottom bar is EN 1.4598 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
200
Elongation at Break, % 18
46
Fatigue Strength, MPa 290
210
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 37
77
Tensile Strength: Ultimate (UTS), MPa 540
600
Tensile Strength: Yield (Proof), MPa 430
230

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 17
15
Thermal Expansion, µm/m-K 6.3
16

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.9
Embodied Water, L/kg 450
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
220
Resilience: Unit (Modulus of Resilience), kJ/m3 950
130
Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 9.5
4.1
Thermal Shock Resistance, points 63
14

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.030
Chromium (Cr), % 0 to 0.2
16.5 to 18.5
Copper (Cu), % 0
1.3 to 1.8
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
60.8 to 70.1
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
2.0 to 2.5
Nickel (Ni), % 0
10 to 13
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0 to 0.1
Oxygen (O), % 0 to 0.18
0
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0.1 to 0.2
Zirconium (Zr), % 91 to 98
0