R60705 Alloy vs. EN 1.5408 Steel
R60705 alloy belongs to the otherwise unclassified metals classification, while EN 1.5408 steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is R60705 alloy and the bottom bar is EN 1.5408 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 190 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 37 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 460 to 1620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 470 |
| Thermal Conductivity, W/m-K | 17 | |
| 48 |
| Thermal Expansion, µm/m-K | 6.3 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 7.8 |
| Embodied Water, L/kg | 450 | |
| 48 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 22 | |
| 16 to 57 |
| Strength to Weight: Bending, points | 22 | |
| 17 to 39 |
| Thermal Diffusivity, mm2/s | 9.5 | |
| 13 |
| Thermal Shock Resistance, points | 63 | |
| 13 to 48 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0 to 0.050 | |
| 0.28 to 0.32 |
| Chromium (Cr), % | 0 to 0.2 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 97.7 to 98.8 |
| Manganese (Mn), % | 0 | |
| 0.8 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0.080 to 0.12 |
| Niobium (Nb), % | 2.0 to 3.0 | |
| 0 |
| Nitrogen (N), % | 0 to 0.025 | |
| 0 |
| Oxygen (O), % | 0 to 0.18 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Zirconium (Zr), % | 91 to 98 | |
| 0 |