R60705 Alloy vs. Solder Alloy 114

Both R60705 alloy and solder alloy 114 are otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is R60705 alloy and the bottom bar is solder alloy 114.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
30
Elongation at Break, % 18
25
Poisson's Ratio 0.34
0.41
Shear Modulus, GPa 37
11
Tensile Strength: Ultimate (UTS), MPa 540
37

Thermal Properties

Latent Heat of Fusion, J/g 250
38
Specific Heat Capacity, J/kg-K 270
170
Thermal Conductivity, W/m-K 17
44
Thermal Expansion, µm/m-K 6.3
26

Otherwise Unclassified Properties

Density, g/cm3 6.7
9.7
Embodied Water, L/kg 450
760

Common Calculations

Stiffness to Weight: Axial, points 8.1
1.7
Stiffness to Weight: Bending, points 23
11
Strength to Weight: Axial, points 22
1.1
Strength to Weight: Bending, points 22
2.6
Thermal Diffusivity, mm2/s 9.5
27
Thermal Shock Resistance, points 63
3.4

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.050
0
Chromium (Cr), % 0 to 0.2
0
Copper (Cu), % 0
0 to 0.080
Gold (Au), % 0
0 to 0.050
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.2
0 to 0.020
Lead (Pb), % 0
58.4 to 60.5
Nickel (Ni), % 0
0 to 0.010
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.18
0
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 0
39.5 to 40.5
Zinc (Zn), % 0
0 to 0.0010
Zirconium (Zr), % 91 to 98
0