R60705 Alloy vs. SAE-AISI 5147 Steel

R60705 alloy belongs to the otherwise unclassified metals classification, while SAE-AISI 5147 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is R60705 alloy and the bottom bar is SAE-AISI 5147 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
190
Elongation at Break, % 18
20
Fatigue Strength, MPa 290
250
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 37
73
Tensile Strength: Ultimate (UTS), MPa 540
600
Tensile Strength: Yield (Proof), MPa 430
360

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 17
46
Thermal Expansion, µm/m-K 6.3
13

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.8
Embodied Water, L/kg 450
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
110
Resilience: Unit (Modulus of Resilience), kJ/m3 950
360
Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 9.5
12
Thermal Shock Resistance, points 63
18

Alloy Composition

Carbon (C), % 0 to 0.050
0.46 to 0.51
Chromium (Cr), % 0 to 0.2
0.85 to 1.2
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
97 to 97.8
Manganese (Mn), % 0
0.7 to 1.0
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.18
0
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0
0.15 to 0.35
Sulfur (S), % 0
0 to 0.040
Zirconium (Zr), % 91 to 98
0