R60705 Alloy vs. SAE-AISI H13 Steel

R60705 alloy belongs to the otherwise unclassified metals classification, while SAE-AISI H13 steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is R60705 alloy and the bottom bar is SAE-AISI H13 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
190
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 37
74
Tensile Strength: Ultimate (UTS), MPa 540
690 to 1820

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 17
29
Thermal Expansion, µm/m-K 6.3
10

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.8
Embodied Water, L/kg 450
78

Common Calculations

Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 22
25 to 65
Strength to Weight: Bending, points 22
22 to 43
Thermal Diffusivity, mm2/s 9.5
7.8
Thermal Shock Resistance, points 63
25 to 65

Alloy Composition

Carbon (C), % 0 to 0.050
0.32 to 0.45
Chromium (Cr), % 0 to 0.2
4.8 to 5.5
Copper (Cu), % 0
0 to 0.25
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
88.8 to 92
Manganese (Mn), % 0
0.2 to 0.5
Molybdenum (Mo), % 0
1.1 to 1.8
Nickel (Ni), % 0
0 to 0.3
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.18
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0.8 to 1.2
Sulfur (S), % 0
0 to 0.030
Vanadium (V), % 0
0.8 to 1.2
Zirconium (Zr), % 91 to 98
0